METACRYLICS PLASTIC SEALER (An Elastomeric Asphalt Sealer & Crack Filler)
Metacrylic's Plastic Sealer is a unique combination of two products, acrylic plastic and asphalt. It is the most durable liquid sealcoat & crack filler product in the industry.
CONTRACTOR'S
Products Analysis |
METACRYLICS PLASTIC SEALER |
GILSONITE |
COAL TAR |
EMULSIONS SS-1h diluted |
APPLICATION
Equipment Required |
Distributor,Spray Rig, squeegee & pushbroom |
Distributor w/adapters |
Squeegee Machine |
Distributor |
WEATHERING
water & sunlight |
Excellent |
Fair |
Good |
Poor |
| Gas & Oil Resistance |
Excellent |
Poor |
Good |
Poor |
| Solvent Resistance |
Excellent* |
None* |
Good |
None* |
| (naptha, white, diesel, & stoklard) *(State of Calif. Dept. of Transportation test results) |
| Volatile Organic Mat. |
18.2gm/l |
250+ gm/l |
100+ gm/l |
10+ gm/l |
| [pollutants in air (approximately)] |
| ELASTICITY |
Excellent |
None |
None |
Poor |
| (expansion & contraction due to surface temperature) |
| ADHESIVE Strength |
Excellent |
Good |
Fair |
Good |
| [binding sand or chips to surface] |
| Flammable and/or Toxic |
No |
Flammable |
Toxic Fumes |
No |
| [binding sand or chips to surface] |
Diluted with Water
Or Solvent |
Water |
Solvent |
Water |
Water |
| Available in Colors |
Yes |
No |
Yes |
No |
ACCELERATED
WEATHERING |
No change observed |
Checking, chalking, & "bronzing" |
N/A |
Failed after 100 hrs by alligatoring |
| [Federal Test #141a, Method 6151, (400 hours exposure)] |
PLASTIC SEALER PRODUCT SPECIFICATIONS
Application Temperature, °F: 110 - 150
Application Rate, gals/sq. yd.: 0.10 - 0.15
Application Rate, gals/100 sq. ft.: 1.1 - 1.66
pH: 8.5 - 9.5
Viscosity, SSF: 15 - 60
Tensile & Elongation Properties -77° F(1)
Elongation, %: 700 min.
Tensile Strength, psi: 10 min.
Tensile & Elongation Properties -77° F(1)
Elongation, %: 700 min.
Tensile Strength, psi: 10 min.
Durability:
Weatherometer, Exposure, hrs.(2): 500 min.
Peel Strength, lb/in(1): 4 min.
(1) 10-15 mil thickness equivalent to application rate of 0.10 gallons per square yard
(2) Specimen shall show no signs of cracking, checking, blistering or peeling after 500 hours exposure to accelerated ultra-violet and moisture weathering.
(3) Peel Strength measured after 150 hours minimum weatherometer exposure.